Other Dielectric Coated Optics

Angle of Incidence (AOI), °: 45
Coatings: HR(R>98%) @ 390 + 780 + 1560 nm

Diameter, mm: Ø25
Material: BK7
Shape: Round
S1 Flatness, PV IR S2 Flatness, PV: <λ/8 @ 632.8 nm
Surface quality, S-D: 20-10
Thickness, mm: 5

4 lateral sides finish: commercial polished
Protective chamfers: <0.25mm@45deg

Coating:
Dimensions tolerance, mm: +/-0,1 mm
Eceptions/remarks:
End surface dimensions: 26x8mm
End surfaces: Flatness LIDT: ≥ 10J/cm2, @ 1064nm; 10ns, 10Hz
Length: 60mm
Material: UVFS
Parallelism error: < 10 arc second
Tilt: 5.5deg
Wave front distortion (including focus): PV ≤ 0.06L per inch @633nm

Clear aperture: >90 %
Coatings:

Diameter, mm: 25.4 mm +0/- 0.5 mm
Group delay dispersion: +/- 100 fs2
Material: Fused Silica
Parallelism error: < 10 arcsec
S1: PR(R=50%+/- 3 %)@ 750-850nm. AOI = 45°. Pol P
S2: AR(Rp<0.25%)@750-850nm
S1 Flatness, PV IR S2 Flatness, PV: L/4 P-V
Surface qulaity: 40-20 S/D
Thickness, mm: 3+/- 0.1 mm

Angle of Incidence (AOI), °: 0
Coatings: S1: HR(R>99.5%)@1047–1064+ AR(R<5%)@950–980; S2: AR(R<0.25%)@950–980.

Diameter, mm: 12.7
Material: UVFS
Shape: Round
S1 Flatness, PV IR S2 Flatness, PV: L/8 (before coating)
Surface quality, S-D: 20-10
Thickness, mm: 2
Wavelength, nm: 950-850+1047-1064

Clear aperture: >90%
Coatings:

Diameter, mm: 12.7 mm (+0.0/-0.1 mm)
Material: UVFS (Corning 7980 (0F)
Parallelism error: <1 arcmin
Protective chamfers: <0.25 mm x 45°
S1: HR(R>99.5%)@ 1047 nm – 1064 nm, + AR(R<5%)@ 950 nm – 980 nm, AOI=0°.
S2: AR(R<0.25%)@ 950 nm – 980 nm, AOI=0°
S1 Flatness, PV IR S2 Flatness, PV: λ/8@ 633 nm, Surface flatness may reduce to 2λ@633 after coating!
Surface quality: 20-20 S-D
Thickness, mm: 2.0 mm (+/-0.1 mm)

Clear aperture: >90%
Coatings:

Diameter, mm: 12.7 mm (+0.0/-0.1 mm)
Material: UVFS (Corning 7980 (0F)
Parallelism error: <1 arcmin
Protective chamfers: <0.25 mm x 45°
S1: HR(R>99.5%)@ 1047 nm – 1064 nm, + AR(R<5%)@ 950 nm – 980 nm, AOI=0°.
S2: AR(R<0.25%)@ 950 nm – 980 nm, AOI=0°
S1 Flatness, PV IR S2 Flatness, PV: λ/8@ 633 nm, Surface flatness may reduce to 2λ@633 after coating!
Surface quality: 20-40 S-D
Thickness, mm: 2.0 mm (+/-0.1 mm)

Protective chamfers: <0.3 mm x 45°
S2: uncoated

S1 Flatness, PV IR S2 Flatness, PV: λ/4 @ 632.8 nm
Thickness, mm: 5 (+/-0.1mm)
S1: HR>99%@ 266+355+532+1064nm, AOI=45°
Material: UVFS (Corning 7980 0F)
LIDT: 15 J/cm2 @ 1064nm, 10ns, 10 Hz
Diameter, mm: 12.7 (+0/-0.1mm)
Coatings:
Clear aperture: >90 %
Surface quality, S1/S2: 40-20 S-D
Parallelism error: < 1 arcmin

Coated surface: 100%
Dimensions A x B x C, mm: 60.3 mm (+0.0/-0.5 mm) x 42.0 mm (+0.0/-0.1 mm)

L1: HRp(Rp>98%) @ 1064 nm + T = 70%(±10%) @ 430-700 nm, AOI = 45°
L2: HR>97-98% @ 532 nm + 1064 nm + HT>60-70% @ 630-670 nm, AOI = 45°
L3: R<1.2% @ 430-670 nm AOI = 45°
Material: UVFS
Parallelism error: <8 arcsec
Protective chamfers: 0.3 mm - 0.5 mm x 45°
Shape: Elliptical
S1 Flatness, PV IR S2 Flatness, PV: <λ/4 @ 632.8 nm
Surface quality, S-D: 60/40
Thickness, mm: 7.0 mm (±0.15 mm)

Material: UVFS
Angle of Incidence (AOI), °: 45

Thickness, mm: 5
Surface quality, S-D: 20-10
S1 Flatness, PV IR S2 Flatness, PV: <λ/8 @ 632.8 nm
Disptach: 8-9 weeks ARO
Diameter, mm: Ø25.4
Coatings: HR(R>98%) @ 1064+532 + HR(R>97%) @ 266+355 nm
Shape: Round

Angle of Incidence (AOI), °: 45
Clear aperture: >90%

Coatings:
Diameter, mm: Ø25.4 (+0/-0.1)
Material: CaF2
S1: HR(R>99.5%)@2280nm+HT(T>95%)@1990nm
S2: AR(R>0.6%)@1990nm
S1 Flatness, PV IR S2 Flatness, PV: <λ/4 @ 632.8 nm
Surface quality, S-D: 60-40
Thickness, mm: 6 (±0.1)

Clear aperture: >90 %
Coatings:

Diameter, mm: 12.7 (+0/-0.1mm)
LIDT: 15 J/cm2 @ 1064nm, 10ns, 10 Hz
Material: UVFS (Corning 7980 0F)
Parallelism error: < 1 arcmin
Protective chamfers: <0.3 mm x 45°
S1: HR>99%@ 266+355+532+1064nm, AOI=45°
S2: uncoated
S1 Flatness, PV IR S2 Flatness, PV: λ/4 @ 632.8 nm
Surface quality, S1/S2: 40-20 S-D
Thickness, mm: 5 (+/-0.1mm)

Center thickness, mm: 2.5mm +/-0.3mm
Centering: <0.4mm

Clear Aperture: 90%
Coatings: AR/AR (R<0.2%) @ 532nm AOI=0deg
Wavelength, nm: 587.6nm
Drawing: MOC 0031
Focal Length Tolerance: +/-2%
Focal length, mm: +130
Material: Corning 7980
Protective chamfers: <0.25mm +/-0.1mm @ 45deg
Size, mm: 9.9x9.9mm +/-0.1mm
Surface figure plano: L/2;
Surface Irregularity, P-V: L/4;
Surface Power cylindrical: 3L/2;
Surface Quality: 20-10 S-D - before coating

S2(PL): AR(R<0,2%)@1063 – 1070 nm, AOI=0 deg
S1(CV): HT(T>98,5%)@1064 – 1070 nm + HR(R>99,8%)@1348 – 1354 nm + HR(R>99,8%)@1535 – 1541 nm, AOI=0 deg

Surface quality: 20-10 S-D (both faces)
S1 Flatness, PV IR S2 Flatness, PV: λ/10 @ 633 nm
Center thickness, mm: 5,0 mm (+/-0,1 mm)
Material: Fused Silica (Suprasil 300)
Clear aperture: >78 % (5,5 mm)
Diameter, mm: 7,0 mm (+0/-0,1 mm)
S1 Flatness, PV IR S2 Flatness, PV: λ/10 @ 633 nm
ROC S1, mm: ROC=-1500 mm (+/-1,5%)
Coatings: