High Contrast 45° Thin Film Polarizers

Center thickness, mm: 2.0+/-0.05mm
Chamfer: 0.5 all round
corners cut: 4x2.5x45deg
S1 Flatness, PV IR S2 Flatness, PV: <λ/[email protected] nm
Length: 11.0+0/-0.1mm
Parallelism error: <1
S1: (HRs>99,8%, HTp>99%)@1061-1067nm, AOI45 (+/-2) +R<33@633,AOI45
S2: HR(Rs>96%)@780-830nm, AOI 30-60deg + AR(Rp<0,5%)@ 1061-1067nm, aoi45+ R(<33%)@633, aoi45deg
Surface quality: 20/10
Width: 9.0+0/-0.1mm

Angle of Incidence (AOI), °: 45
Clear aperture: >90
Dimensions tolerance, mm: +0/-0.1
Dimensions, mm: 50.8
Material: UVFS
Protective chamfers: <0.25 mm x 45°
Surface quality, S-D: 20-10
Thickness tolerance, mm: ±0.1
Thickness, mm: 6
Transmission p-pol, %: >95
Transmission s-pol, %: <1
Wavelength, nm: 1350
Wedge / Parallelism error: <30 arcsec

Thickness, mm: 5 (±0.1)
Angle of Incidence (AOI), °: 45 (angle tunning ±1.5)
Clear Aperture: >90
Dimensions, mm: Ø25.4 (+0/-0.1)
Extinction Ratio: >1000:1
Material: UVFS
Protective chamfers: 0.1-0.3 mm x 45°
Surface quality, S-D: 20-10
Typical LIDT: 7.1 J/cm² (s-pol); 3.2 J/cm² (p-pol) @ 1064 nm, 12 ns, 100 Hz;
Transmission p-pol, %: >97
Transmission s-pol, %: <0.1
Transmitted wavefront distortion, PV: <λ/8 @ 632.8 nm
Wavelength, nm: 1064
Wedge / Parallelism error: <30 arcsec

Thickness, mm: 5 (±0.1)
Angle of Incidence (AOI), °: 45 (angle tunning ±1.5)
Clear Aperture: >90
Dimensions, mm: Ø25.4 (+0/-0.1)
Extinction Ratio: >500:1
LIDT: >4 J/cm² @ 355 nm; 10 ns; 10 Hz for s-pol & >1 J/cm² @ 355 nm; 10 ns; 10 Hz for p-pol;
Material: UVFS
Protective chamfers: 0.2-0.3 mm x 45°
Surface quality, S-D: 20-10
Transmission p-pol, %: >97
Transmission s-pol, %: <0.2
Transmitted wavefront distortion, PV: <λ/8 @ 632.8 nm
Wavelength, nm: 355
Wedge / Parallelism error: <30 arcsec

Thickness, mm: 5 (±0.1)
Material: UVFS
Wavelength, nm: 1064
Transmitted wavefront distortion, PV: <λ/8 @ 632.8 nm
Surface quality, S-D: 20-10
S2: N/A
Parallelism error: <30 arcsec
LIDT for Rs: >10 J/cm2, 10 ns, 10 Hz, 1064 nm
Extinction Ratio: >1000:1
Dimensions, mm: 20 x 50 (+0/-0.1)
Coatings:
Clear Aperture: >90
S1: Pol (Tp>99%, Rs>99.9%) @1064, AOI=45 deg (±1°)

Thickness, mm: 5 (±0.1)
Transmission p-pol, %: >97.5
Wavelength, nm: 532
Transmitted wavefront distortion, PV: <λ/8 @ 632.8 nm
Angle of Incidence (AOI), °: 45 (angle tunning ±1.5)
Transmission p-pol, %: >98
Typical LIDT: 15 J/cm² (s-pol); 7 J/cm² (p-pol) @ 1064 nm, 12 ns, 100 Hz
Protective chamfers: 0.1-0.3 mm x 45°
Parallelism error: <30 arcsec
Material: UVFS
Extinction Ratio: ~ 1000:1 (with angular adjustment of ±1.5°)
Dimensions, mm: Ø25.4 (+0/-0.1)
Clear Aperture: >90
Clear Aperture: 90
Surface quality, S-D: 20-10
Transmission s-pol, %: <0.2