Axis orientation: c-cut (+/-2°)
Clear aperture: >90%

Coatings: e-Beam
Diameter, mm: 15.0 mm (+0.0/-0.1 mm)
Material: MgF₂ (UV Grade, monocrystalline material)
Parallelism error: <3 arcmin
Protective chamfers: <0.25 mm x 45°
S1: AR(R<0.5%)@258 nm, AOI=0°
S2: AR(R<0.5%)@258 nm, AOI=0°
Surface quality, S1/S2: 20/10 S/D
Thickness, mm: 2.0 mm (+/-0.1 mm)
Transmitted WFD, P-V: <λ/10@633 nm per CA

Material: MgF₂ (monocrystalline, C-cut)
Transmitted wavefront distortion, PV: <λ/4@633 nm per Ø38.1

Thickness, mm: 3.0 mm (+/-0.1 mm)
Surface quality, S1/S2: 20/10 S/D (after coating 40/20 S/D)
S2: BBAR(R<1.2%)@400 nm - 650 nm, AOI=0°
S1: BBAR(R<1.2%)@400 nm - 650 nm, AOI=0°
Clear aperture: >90%
Parallelism error: <3 arcmin
LIDT: >5 J/cm² @1064 nm, 10 ns, 10 Hz
Your part:
Diameter, mm: 50.8 mm (+0.0/-0.1 mm)
Coatings: e-Beam
Protective chamfers: <0.25 mm x 45°

Thickness, mm: 3.0 mm (+/-0.1 mm)
Clear aperture: >90%

Transmitted wavefront distortion, PV: <λ/4@633 nm per Ø38.1
Surface quality, S1/S2: 20/10 S/D (after coating 40/20 S/D)
S2: BBAR(R<1.5%)@700 nm - 1300 nm, AOI=0°
S1: BBAR(R<1.5%)@700 nm - 1300 nm, AOI=0°
Protective chamfers: <0.25 mm x 45°
Parallelism error: <3 arcmin
Material: MgF₂ (monocrystalline, C-cut)
LIDT: >5 J/cm² @1064 nm, 10 ns, 10 Hz
Your part:
Coatings: e-Beam
Diameter, mm: 50.8 mm (+0.0/-0.1 mm)

S1: BBAR(R<1.5%)@700 nm - 1300 nm, AOI=0°
Thickness, mm: 1.0 mm (+/-0.1 mm)

Transmitted wavefront distortion, PV: <λ/4@633 nm per CA
Surface quality, S1/S2: 20/10 S/D (after coating 40/20 S/D)
S2: BBAR(R<1.5%)@700 nm - 1300 nm, AOI=0°
Protective chamfers: <0.25 mm x 45°
Parallelism error: <3 arcmin
Material: MgF₂ (monocrystalline, C-cut)
Clear aperture: >90%
LIDT: >5 J/cm² @1064 nm, 10 ns, 10 Hz
Coatings: e-Beam
Diameter, mm: 25.4 mm (+0.0/-0.1 mm)
Your part:

Wavelength, nm: 1100
Mount:
S1: BBAR(R<1%)@1100 nm - 2200 nm, AOI=0°
Transmitted wavefront distortion, PV: <λ/8@633 nm
Thickness tolerance, mm: +0.0/-0.1 mm
Surface quality, S1/S2: 40/20 S/D
S2: BBAR(R<1%)@1100 nm - 2200 nm, AOI=0°
Retardation: λ/2 @1100 nm – 2200 nm
Retardation tolerance: +/- λ/50 @20°C
Parallelism error: <30 arcsec
Material: Crystalline Quartz + MgF₂
LIDT: >5J/cm² for 10 ns pulses @1064 nm
Diameter tolerance, mm: +0.0/-0.1 mm
Coatings:
Clear aperture: >20.0 mm diameter of the center