In stock
LIDT: >2 J/cm² @ 800 nm; 300 ps; 10 Hz
Coatings on S1: HR(R>99.7%)@750-850nm
Wedge / Parallelism error: <5 arcmin
Thickness, mm: 6 (±0.5)
Surface quality, S-D: 10-5 before coating
Material: UVFS
LIDT: >1 J/cm² @ 800 nm; 300 ps; 10 Hz
Group Delay Dispersion: < ± 100 fs² over 750-850nm
S1 Flatness, PV IR S2 Flatness, PV: <λ/6 @ 632.8 nm
Coatings on S2: AR(R<0.3%)@750-850nm
Clear aperture: >90%
Angle of Incidence (AOI), °: 0
Adhesion and durability: Per MIL-C-675A
Dimensions, mm: Ø25.4 (+0/‐0.5)
Coatings on S1: HR(R>99.7%)@750-850nm
Wedge / Parallelism error: <5 arcmin
Thickness, mm: 6 (±0.5)
Surface quality, S-D: 10-5 before coating
Material: UVFS
LIDT: >1 J/cm² @ 800 nm; 300 ps; 10 Hz
Group Delay Dispersion: < ± 100 fs² over 750-850nm
S1 Flatness, PV IR S2 Flatness, PV: <λ/6 @ 632.8 nm
Coatings on S2: AR(R<0.3%)@750-850nm
Clear aperture: >90%
Angle of Incidence (AOI), °: 0
Adhesion and durability: Per MIL-C-675A
Dimensions, mm: Ø25.4 (+0/‐0.5)