In stock
Clear Aperture: >90
Clear aperture: > 90 %
Coatings:
Diameter, mm: 25.4 mm (+0/-0.1 mm)
Dimensions, mm: Ø25.4 (+0/-0.1) x 5 (±0.1)
LIDT: 10 J/cm2 @1064 nm, 10 ns, 10 Hz
LIDT: 10 J/cm² 1064 nm, 10 ns
Material: UVFS
Material: UVFS (Corning 7980 0F)
Parallelism error: <1 arcmin
S1(IBS ^): HRsp>99.95%, GDD<20 fs2 @ 1010-1050 nm, AOI 45°, Nb2O5, SiO2
S1(IBS, ^): HRsp>99.95%, GDD<20 fs² @ 1010-1050 nm, AOI=45°
S1: HRsp>99.95%, GDD<20 fs² @ 1010-1050 nm, AOI=45°
S2: polished, uncoated
S2: uncoated
Surface flatness after coating: S1: <λ/8 @ 632.8 nm per 6 mm diameter at any point in CA
Surface flatness before coating: S1: <λ/8 @ 632.8 nm per CA
S1 Flatness, PV: <λ/8@ 632.8 nm on each 6 mm diameter area in clear aperture
Surface quality after coating, S1: 20/10 S/D, S2: best effort (but 60/40 acceptable) S/D
Surface quality before coating, S1: 20/10 S/D, S2: best effort (but 60/40 acceptable) S/D
S2 Surface quality, S-D: commercially polished
S1 Surface quality, S-D: 20-10 S-D
Thickness, mm: 5 mm (+/-0.1 mm)
Clear aperture: > 90 %
Coatings:
Diameter, mm: 25.4 mm (+0/-0.1 mm)
Dimensions, mm: Ø25.4 (+0/-0.1) x 5 (±0.1)
LIDT: 10 J/cm2 @1064 nm, 10 ns, 10 Hz
LIDT: 10 J/cm² 1064 nm, 10 ns
Material: UVFS
Material: UVFS (Corning 7980 0F)
Parallelism error: <1 arcmin
S1(IBS ^): HRsp>99.95%, GDD<20 fs2 @ 1010-1050 nm, AOI 45°, Nb2O5, SiO2
S1(IBS, ^): HRsp>99.95%, GDD<20 fs² @ 1010-1050 nm, AOI=45°
S1: HRsp>99.95%, GDD<20 fs² @ 1010-1050 nm, AOI=45°
S2: polished, uncoated
S2: uncoated
Surface flatness after coating: S1: <λ/8 @ 632.8 nm per 6 mm diameter at any point in CA
Surface flatness before coating: S1: <λ/8 @ 632.8 nm per CA
S1 Flatness, PV: <λ/8@ 632.8 nm on each 6 mm diameter area in clear aperture
Surface quality after coating, S1: 20/10 S/D, S2: best effort (but 60/40 acceptable) S/D
Surface quality before coating, S1: 20/10 S/D, S2: best effort (but 60/40 acceptable) S/D
S2 Surface quality, S-D: commercially polished
S1 Surface quality, S-D: 20-10 S-D
Thickness, mm: 5 mm (+/-0.1 mm)